Name: Multi-layer PA Tube
Type:
Product Specifications:
|
Show Details:
lron Horse recent development of automotive fuel systems:having imported advanced multi-layer extrusion lines and technology.The tube has excellent resistance to permeation,oil,corrosion and anti-aging.It applies to the mixtrue of fuel and ethanol,which can meet Euro IV.It is a kind of lightweight,high performance and environmentally friendly tube widely used in automotive fuel system.
Five-layer tube with OD6mm,8mm,10mm etc.
Out Layer PA12
Tie Layer
Barrier Layer EVOH
Tie Layer
lnner Layer PA12
Executive Standard:SAE J2260 QC/T798-2008
Working temperature-40℃~115℃
Continuous working temperature≤90℃
Working pressure:≤0.7MPa
No
|
|
Test project
|
unit
|
requirement
|
1
|
Burst strength
|
burst strength in room temperature
|
MPa
|
≥5.6
|
burst strength in High temperature
|
MPa
|
≥2.1
|
2
|
Bending performance
|
min.Bending radius
|
mm
|
Meet QCT-798-2008 requirements
|
Resistance to bending deformation
|
--
|
|
Burst strength after bending
|
MPa
|
≥5.6
|
3
|
Resistance to ZnCl2
|
apperance
|
--
|
no cracking with oyter and inner tube surface
|
burst strength in room temperature
|
MPa
|
≥4.2
|
4
|
Cold-temp erature impact
|
apperance
|
--
|
no cracking in apperacnce
|
burst strength in room temperature
|
MPa
|
≥4.2
|
5
|
performance of permeation resistance
|
permeation rate
|
g/m.d
|
<0.05
|
length change rate
|
--
|
-1%~+1%
|
burst strength in room temperature
|
MPa
|
≥5.6
|
6
|
yield stress
|
parallel Extrusion direction
|
N/m㎡
|
≥24
|
vertical Extrusion direction
|
|
≥25
|
elongation
|
Extrusion direction
|
%
|
≥170
|
vertical direction
|
%
|
≥170
|
7
|
Performance of fuel resistance
|
apperance
|
--
|
no cracking in apperacnce
|
Low-temperature impact
|
--
|
no cracking in apperacnce
|
burst strength in room temperature
|
MPa
|
≥5.6
|
Stress yield at Extrusion direction
|
N/m㎡
|
≥20
|
Elongation at Extrusion direction
|
%
|
≥150
|
layer adhesive force
|
|
no clear delamination phenomenon between cutting layers
|