Name: Fuel Line Hose
Type:
Product Specifications:
|
Show Details:
Material: FKM/ECO/Aramid or polyester /ECO/FKM
Construction: spiral
Appearance: black, surface of the fabric pattern/mill finish
Operating temperature: -40℃~135℃/150℃
Executive standard: SAE J30R7 GBT 24141.2-2009
Specification:
Nominal Size(mm)
|
Tolerance I.D(mm)
|
Tolerance O.D(mm)
|
Working strength(MPa)
|
Burst strength(min)
|
Min. bend radius (mm)
|
5.5
|
5.5±0.3
|
11.5±0.5
|
0.7
|
3.0
|
44
|
6
|
6.0±0.3
|
12.0±0.5
|
0.7
|
3.0
|
48
|
7.5
|
7.5±0.3
|
14.5±0.5
|
0.7
|
3.0
|
60
|
Property:
No
|
Item
|
Condition
|
Requirement
|
1
|
vacuum collapse flat
|
internal pressure80KPa(absolute pressure)
|
diameter decrease≤20%
|
2
|
cold temperature flexibilityt
|
-40℃,24h,bending
|
out layer without cracking and fine lines 1MPa/1min ensure no leaking in the test
|
3
|
physical properties of green material
|
tensile strength of out rubber
|
min. 10MPa
|
tensile strength of inner or middle rubber
|
min. 10MPa
|
elongation rate of out rubber
|
min. 250%
|
elongation rate of inner rubber
|
min. 250%
|
4
|
dry and heat aging resistance
|
135℃,1000h
|
inner and outer hose without cracking, carbonization and cracks
|
5
|
fuel resistance (inner rubber)
|
23℃,168h,CM15
|
volume change rate max. +25% / variation of tensile strength max. -40%
|
23℃,168h,CM85
|
6
|
oxidized fuel resistance (inner rubber)
|
23℃,168h,CM15
|
variation of tensile strength max. -40%
|
23℃,168h,CM85
|
7
|
fuel resistance(out rubber)
|
IRM 903oil,135℃,70h
|
volume change max. +15%
|
8
|
extract test
|
|
Total lipid extract max. 0.2g/m2
|
9
|
ozone resistance(out rubber)
|
100pphm,40℃,70h
|
no racking
|
10
|
initial adhesion
|
each layer
|
min. 1.4N/mmglue material fracture
|
11
|
fuel oil aging adhesive
|
CM15 ,40℃,1000h ;70℃,24h
|
min. 1.4N/mmglue material fracture
|
12
|
kink test
|
|
ball pass through the tube freely
|
13
|
permeation test
|
CM15 ,60℃,664h 40℃,1000h
|
68.75g/m2/day
|